This paper presents the results of two experimental tests on masonry barrel vault with fill material. The vault was built of clay bricks and lime mortar. Thickness, internal span and rise of the vaults were 125 mm, 2000 mm and 730 mm respectively. Light expanded clay aggregate was used as a fill material. The fill depth at the crown was 200 mm. The first test was performed on unstrengthened vault. In this case the main aims were to determine load-carrying capacity and examine the collapse mechanism of vault with backfill. In order to perform the second test the arch used in the first test was strengthened externally and tested again. The aims of this test was to determine load-carrying capacity and examine the general behavior of strengthened barrel vaults with fill material. Results of both tests were compared. The presence of strengthening influenced on load-carrying capacity and ductility of the vault. The strengthened element had higher failure load and was more ductile then vault without strengthening.
W artykule przedstawiono wyniki badań eksperymentalnych sklepień z pachami wypełnionymi materiałem zasypowym. Elementy murowano z ceramicznej cegły pełnej na zaprawie wapiennej a zasypkę wykonano z keramzytu. Badania przeprowadzono na pasmach sklepień walcowych rozpiętości w świetle podpór wynoszącej 2000 mm, grubości 125 mm i strzałce 730 mm. Sklepienia obciążano w 1/4 rozpiętości aż zniszczenia rejestrując deformacje i poziom siły niszczącej. W pierwszym badaniu testowano sklepienie bez wzmocnienia wyznaczając jego nośność oraz identyfikując mechanizm zniszczenia. Po badaniu sklepienie wzmocniono powierzchniowo siatką z włókien szklanych i ponownie poddano testom. Celem badania było wyznaczenie obciążenia niszczącego oraz poznanie pracy sklepienia wzmocnionego z zasypką. Sklepienie wzmocnione charakteryzowało się większą nośnością i większą zdolnością do deformacji pod obciążeniem niż przed wzmocnieniem.