High-performance Cr–Zr–O and Cr–Zr–K–O catalysts prepared by nanocasting for dehydrogenation of propane to propene / A. Węgrzyniak, A. Rokicińska, E. Hędrzak, B. Michorczyk, K. Zeńczak-Tomera, ... więcej

High-performance Cr–Zr–O and Cr–Zr–K–O catalysts prepared by nanocasting for dehydrogenation of propane to propene / A. Węgrzyniak, A. Rokicińska, E. Hędrzak, B. Michorczyk, K. Zeńczak-Tomera, P. Kuśtrowski, P. Michorczyk // Catalysis Science & Technology [Dokument elektroniczny]. – 2017, Vol. 7, Iss. 24, s. 6059-6068 : tab., wykr. – Tryb dostępu: http://pubs.rsc.org/en/content/articlelanding/2017/cy/c7cy01744h#!divAbstract. – Bibliogr. 62 poz., Streszcz. ang. – doi: 10.1039/C7CY01744H. – ISSN 2044-4761

Ordered mesoporous Cr–Zr–O and Cr–Zr–K–O catalysts were prepared by nanocasting using a CMK-3 carbon replica as a hard template. The synthesized oxide nanoreplicas had a uniform pore-size distribution ... więcej

Ordered mesoporous Cr–Zr–O and Cr–Zr–K–O catalysts were prepared by nanocasting using a CMK-3 carbon replica as a hard template. The synthesized oxide nanoreplicas had a uniform pore-size distribution centered in the range of 5.5–6.5 nm and specific surface areas of 123–164 m2 g−1. Results of physicochemical characterization (UV-vis DRS, EPR, XRD, XPS and H2-TPR) revealed that chromium species were stabilized in +3, +5 and +6 oxidation states in all samples. The developed materials exhibited excellent catalytic performance and much higher resistance to deactivation during the process of dehydrogenation of propane to propene in comparison with a material prepared without the CMK-3 hard template assistance. Potassium doping (0.2, 0.5 or 1.0 wt%) of the catalyst with a Zr/Cr atomic ratio of 5 enhanced the selectivity to propene and resistance to coke deposition.